Preparation, Characterization, and Biological Properties of Hydroxyapatite from Bigeye Snapper (Priancanthus tayenus) Bone.

The optimum condition of acid hydrolysis for hydroxyapatite extraction from bigeye snapper (Priancanthus tayenus) bone and the effects of extraction time (10-60 min) and HCl concentration (2.0-5.0% w/v) on yield and hydroxyapatite properties were determined. The optimum extracted condition was found using 5% HCl for 60 min, which was 13.4% yield; 19.8 g/100 g Ca content; 9.6 g/100 g P content; 2.1 Ca/P ratio; L*, a*, b*; and ΔE as 84.5, 2.8, 16.5, and 15.6, respectively. The using of 5% NaOH solution was optimum for hydroxyapatite precipitation from the extracted solution. The characteristic and biological properties of the obtained hydroxyapatite were studied. Fourier transform infrared spectroscopy and X-ray diffraction results showed a good comparison between the extracted and commercial hydroxyapatite. The microstructure of the extracted hydroxyapatite from a scanning electron microscope showed an irregular and flat-plate shape, large surface area, and roughness. The extracted hydroxyapatite was non- and low-cytotoxicity at a concentration of 50 and 100-400 µg/mL, respectively. Bovine serum albumin (BSA) adsorption and desorption of hydroxyapatite was studied. An increasing BSA concentration, hydroxyapatite amount, and adsorption time significantly increased protein adsorption on hydroxyapatite. Protein desorption from BSA-loaded hydroxyapatite showed an increase of release initially in the first 4 days and became a steady release rate until 14 days.